MIG WIRE 310L S/S 1.2MM
Part No: M31012
These consumables are used primarily for welding similar wrought or
cast 25%Cr-20%Ni (310) parent alloys with up to 0.25% carbon. Parent
metal and weld metal are fully austenitic, unlike the other common 300
series stainless steels. For maximum resistance to solidification
cracking and microfissuring, the MMA weld metal manganese range is
raised to 2-5% in accordance with European practice.
The high alloy content of type 310 gives useful oxidation resistance up to peak temperatures of about 1200?C for heat shields, furnace parts and ducting.
These consumables can also be used for mixed welding and dissimilar joints including those where PWHT is applied, but it should be noted that the relatively high thermal expansion coefficient may promote thermal fatigue in transition joints which are subject to thermal cycling. In such cases, nickel base consumables are usually preferred. This product is priced “per KG”. The minimum quantity available to purchase is shown in the "Pack Qty".
The high alloy content of type 310 gives useful oxidation resistance up to peak temperatures of about 1200?C for heat shields, furnace parts and ducting.
These consumables can also be used for mixed welding and dissimilar joints including those where PWHT is applied, but it should be noted that the relatively high thermal expansion coefficient may promote thermal fatigue in transition joints which are subject to thermal cycling. In such cases, nickel base consumables are usually preferred. This product is priced “per KG”. The minimum quantity available to purchase is shown in the "Pack Qty".