MIG WIRE CORED

Applications

• Multi-layer welding of structural steels, offshore
  structures and thick, windmill, pressure vessels.

• Good weldability for all range of thickness of plate.
  Excellent impact value and crack-resistibility of welded metal.
  Inactive type flux is not affected by welding parameter, especially
  suitable for multi-layer welding of thick plate.

1. Dry the flux at 300~350?(572~662?) for 60minutes before use.


2. For the first layer in groove, keep the current and speed
   low in the case of multi-layer welding.
   
   

• Classification AWS A5.20/E717-1CHB/T-9M


• All positional Rutile based Flux Cored Wire


• Excellent usability with stable arc


• Superior wire feed properties


• Recommended shielding gas: Argon+CO² mix or 100% CO²

• Classification AWS A5.20/E717-1CHB/T-9M


• All positional Rutile based Flux Cored Wire


• Excellent usability with stable arc


• Superior wire feed properties


• Recommended shielding gas: Argon+CO² mix or 100% CO²

Application

• All position welding of building, shipbuilding, bridge
  construction machinery, and vehicles.

• SC-71LHM Cored is a titania type flux cored wire for all
  position welding. It has extra low hydrogen level(H5) and provides an
  exceptionally smooth and stable arc with a fast freezing slag system.

1. Proper Preheating (50~150°C) (122~302°F) and interpass
   temperature must be used in order to release hydrogen which may cause
   cracking in weld metal when electrodes are used for medium and heavy
   plates.


2. One-side welding defects such as hot cracking may occur
   with wrong welding parameter such as high welding speed.


3. Use Ar + 20~25% CO2gas.
   
   

Applications

• All position welding in shipbuilding, machinery, bridges,
  buildings, vehicles using mild and higher strength steels.

• SF-71LF is the most widely used titania type flux cored
  wire for all position welding with CO2 shielding gas.


• As deposition rate is higher than solid wire and manual
  metal arc electrode, highly efficient welding can be performed.


• Arc stability is excellent. Spatter loss is low and slag
  covering is uniform with good removability.


• Fume generation is lower than conventional flux cored wires.


• SF-71LF is effective for use in insufficient ventilation
  areas.
  
  

1. Proper preheating(50~150°C)(122~302 ) and interpass
   temperature must be used in order to release hydrogen which may cause
   cracking in weld metal when electrodes are used for medium and heavy
   plates.


2. One-side welding defects such as hot cracking may occur
   with wrong welding parameter such as high welding speed.


3. Use 100% CO2 gas

Applications and Features:

• BW-70C-6M is a metal type flux cored wire and designed for
  positional welding by single pass & multi pass with 70-85%
  Ar+15-25% Co2 mixed gas shielding.


• BW70C-6M is suited to Butt and fillet welding of mild steel
  & 50kgf/mm2 high tensile strength of structures, such as
  vehicle and industrial machinery.
  
  

• Arc stability


• Low spatters


• Good wire feed ability


• Good Bead appearance


• Excellent Slag removal


• Low Fume


• Very High deposition rate – Good welding efficiency like
  solid wire
  
  

• BW70C-6M is a full iron powder cored wire recommended for a
  wide range of high speed fillet and butt welding applications in all
  downhand positions. BW70C-6M 1.2mm can also be used in “short arc” or
  pulsed transfer mode to facilitate welding in all positions.

• Argon+ CO2 blend

• ABS, DNV(CO2,Mixed Gas)

Applications

• Multi-layer welding of structural steels, offshore
  structures and thick, windmill, pressure vessels.

• Good weldability for all range of thickness of plate.
  Excellent impact value and crack-resistibility of welded metal.
  Inactive type flux is not affected by welding parameter, especially
  suitable for multi-layer welding of thick plate.

1. Dry the flux at 300~350?(572~662?) for 60minutes before use.


2. For the first layer in groove, keep the current and speed
   low in the case of multi-layer welding
   
   

Applications

• All position welding for ship hulls, vehicles, bridges,
  chemical plant machinery and other metal fabrication.
  
  

• SF-71MC is a titania type flux cored wire applicable for
  all-position welding by 100%CO2 shielding gas or 75%Ar+25%CO2 shielding
  gas. Less spattering and good slag removability shorten the time of
  bead grinding operation
  
  

1. Proper preheating 50~150°C(122~302 ) and interpass
   temperature must be used in order to release hydrogen which may cause
   cracking in weld metal when electrodes are used for medium and heavy
   plates.


2. Use 100% CO2 gas or Ar-CO2 Mixture.

Applications

• Building, shipbuilding, bridge construction, machinery, and
  vehicles.

• Despite welding position, will get low spatter, soft arc,
  good bead appearance and excellent weldability with this wire.

1. Proper preheating(50~150°C)(122~302 ) and interpass
   temperature must be used in order to release hydrogen which may cause
   cracking in weld metal when electrodes are used for medium and heavy
   plates.


2. One-side welding defects such as hot cracking may occur
   with wrong welding parameter such as high welding speed.


3. Use Ar+20~25% CO2 gas
   
   

Applications

• All position welding for ship hulls, vehicles, bridges,
  chemical plant machinery and other metal fabrication.
  
  

• SF-71MC is a titania type flux cored wire applicable for
  all-position welding by 100%CO2 shielding gas or 75%Ar+25%CO2 shielding
  gas. Less spattering and good slag removability shorten the time of
  bead grinding operation
  
  

1. Proper preheating 50~150°C(122~302 ) and interpass
   temperature must be used in order to release hydrogen which may cause
   cracking in weld metal when electrodes are used for medium and heavy
   plates.


2. Use 100% CO2 gas or Ar-CO2 Mixture.

Applications

• Supercored 70NS is used for welding in shipbuilding,
  machinery, bridge Construction, structural fabrication, automated of
  robotic welding

• Supercored 70Ns is a metal- cored wire which combines the
  high deposition rate of FCW with the high efficiencies of solid wire,
  provides exceptionally smooth and stable arc, low spatter and minimal
  slag coverage.
  
  

• Proper preheating(50~ 150?) and interpass temperature must
  be used in order to release hydrogen which may cause cracking in weld
  metal when electrodes are used for medium and heavy plates.


• One- side welding defects such as hot cracking in may occur
  with wrong welding parameter such as high welding speed.


• Use Ar + 20- 25% CO2 gas.
  
  

Application

• All position welding of building, shipbuilding, bridge
  construction machinery, and vehicles.

• SC-71LHM Cored is a titania type flux cored wire for all
  position welding. It has extra low hydrogen level(H5) and provides an
  exceptionally smooth and stable arc with a fast freezing slag system.

1. Proper Preheating (50~150°C) (122~302°F) and interpass
   temperature must be used in order to release hydrogen which may cause
   cracking in weld metal when electrodes are used for medium and heavy
   plates.


2. One-side welding defects such as hot cracking may occur
   with wrong welding parameter such as high welding speed.


3. Use Ar + 20~25% CO2gas.
   
   

Applications

• Supercored 70MXH is a metal cored wire for high speed
  single or twin tandem welding application in the flat and horizontal
  fillet position. This wire benefits from high deposition rate and is
  widely used for shipbuilding, construction of bridge, and structural
  fabrication.
  
  

• Supercored 70MXH has very low spatter loss rate and minimum
  amount of slag. It gives excellent penetration and good arc stability.
  Especially has good anti-porosity to zinc-primer plate and mill scale
  plate in high speed single and twin tandem fillet welding.
  
  

1. Proper preheating(50~150°C)(122~302 ) and interpass
   temperature must be used in order to release hydrogen which may cause
   cracking in weld metal when electrodes are used for medium and heavy
   plates.


2. Use 100% CO2 gas
   
   

Dual Shield II 712X is an all-position flux cored wire intended for
applications requiring outstanding weld metal toughness. This X Series
wire, in combination with 75% Argon/25% CO2 shielding gas, can produce
Charpy V-notch impact results of more than 50 ft-lb (68 J) at -60°F
(-51°C) and Crack Tip Opening Displacement (CTOD) results of more than
20 mils (0.5 mm) at -40°F (-40°C). Dual Shield II 712X also provides
the smooth arc and low spatter levels characteristic of Dual Shield
flux cored wires.

Applications include off-shore oil components, shipbuilding and heavy
equipment where exceptional Charpy impact/low temperature toughness is
required.



Industries

• Heavy Equipment


• Offshore Oil


• Ship/Barge Building
  
  

• Welding-FCAW - Flux Core Arc Welding

http-equiv="content-type">



Applications

• Vertical- up butt welding of side shells and inner
  structures of ships, Plates of storage tank and web members of box-
  girders of bridges.
  
  

• SC- EG2 cored is a small diameter flux cored wire to be
  used with CO2 shielding gas for electro gas arc welding at high speed.
  The arc is stable and has good bead appearance. It provides highly
  efficient welding by electro gas process.
  
  

• Use 100% CO2 gas.

Applications

• Supercored 70NS is used for welding in shipbuilding,
  machinery, bridge Construction, structural fabrication, automated of
  robotic welding

• Supercored 70Ns is a metal- cored wire which combines the
  high deposition rate of FCW with the high efficiencies of solid wire,
  provides exceptionally smooth and stable arc, low spatter and minimal
  slag coverage.
  
  

• Proper preheating(50~ 150?) and interpass temperature must
  be used in order to release hydrogen which may cause cracking in weld
  metal when electrodes are used for medium and heavy plates.


• One- side welding defects such as hot cracking in may occur
  with wrong welding parameter such as high welding speed.


• Use Ar + 20- 25% CO2 gas.
  
  

Applications

• Supercored 70NS is used for welding in shipbuilding,
  machinery, bridge Construction, structural fabrication, automated of
  robotic welding

• Supercored 70Ns is a metal- cored wire which combines the
  high deposition rate of FCW with the high efficiencies of solid wire,
  provides exceptionally smooth and stable arc, low spatter and minimal
  slag coverage.
  
  

• Proper preheating(50~ 150?) and interpass temperature must
  be used in order to release hydrogen which may cause cracking in weld
  metal when electrodes are used for medium and heavy plates.


• One- side welding defects such as hot cracking in may occur
  with wrong welding parameter such as high welding speed.


• Use Ar + 20- 25% CO2 gas.
  
  

Applications and Features:

• BW-71T-1 is a titania type flux cored wire and designed for
  all-position welding by single pass & multi pass with
  CO& mixed gas shielding.


• BW71T-1 is suited to Butt and fillet welding of mild steel
  & 490N/mm2 high tensile strength steels of structure such as
  ships, bridges, buildings and storage tanks etc.
  
  

• Arc stability


• Low spatters


• Good wire feed ability


• Good Bead appearance


• Excellent Slag removal


• Low Fume


• High deposition rate – Good welding efficiency
  
  

• All positions.

• CO2 and Argon+ CO2 blend

• CO2 Shielding Gas: ABS, BV, DNV, GL, KR, LR, NK, RINA, CWB,
  TUV


• MIX Shielding gas: ABS, BV, DNV, GL, LR, NK, RINA, CWB, TUV
  
  

Applications and Features:

• BW-71T-1 is a titania type flux cored wire and designed for
  all-position welding by single pass & multi pass with
  CO& mixed gas shielding.


• BW71T-1 is suited to Butt and fillet welding of mild steel
  & 490N/mm2 high tensile strength steels of structure such as
  ships, bridges, buildings and storage tanks etc.
  
  

• Arc stability


• Low spatters


• Good wire feed ability


• Good Bead appearance


• Excellent Slag removal


• Low Fume


• High deposition rate – Good welding efficiency
  
  

• All positions.

• CO2 and Argon+ CO2 blend

• CO2 Shielding Gas: ABS, BV, DNV, GL, KR, LR, NK, RINA, CWB,
  TUV


• MIX Shielding gas: ABS, BV, DNV, GL, LR, NK, RINA, CWB, TUV
  
  

Description

• A rutile flux cored all position wire designed for welding
  mild and carbon steels, especially when good impact toughness is
  required at sub zero temperatures. Ideal for single and multi-pass
  applications, it delivers outstanding welding performance and produces
  high quality X-ray clear weld deposit with a bead contour that is flat
  to slightly convex.


• It performs exeptionally well over rust, mill scale and
  some primers with no pre-cleaning of the steel necessary.


• Formula XL-525 has outstanding mechanical properties that
  resemble those of E7018 MMAW (SMAW) electrodes, plus high operator
  appeal with low fume levels, low spatter and easy slag removal.
  
  

• Recommended for ship building, storage vessels, off-shore
  structures, earth moving equipment and pipe welding.